Waspaloy is Ni-Cr-Co based superalloy.Excellent mechanical properties below 980 ° C (1800 ° F), high strength and oxidation resistance at 760-870 ° C (1400-1600 ° F).
Its strength is superior to that of alloy 718 at temperature above 1200-1300℉(650-750℃), and is generally comparable to Haynes R-41 alloy.
Waspaloy Material Composition
| C | Cr | Mo | Ni | Co | Al | Ti | Fe | Si | Mn | P | S | B | Zr | Cu |
| 0.03-0.1 | 18-21 | 3.5-5 | Balance | 12-15 | 1.2-1.6 | 2.75-3.25 | ≤2 | ≤0.15 | ≤0.1 | ≤0.015 | ≤0.015 | 0.003-0.01 | 0.02-0.08 | ≤0.1 |
Waspaloy Material Mechanical Properties
| Grade | Density | Melting Point | Mechanical Property | |||||
| Temperature | Tensile Strength | Yield Strength | Elogation min | Ψ min | Hardness min | |||
| Waspaloy | 8.22 |
1330-1360℃ 2426-2480℉ |
815℃ 1499℉ |
608 Mpa | / | 20 | 32 | 299-387 HBS |
Applications of Waspaloy
Gas Turbine Blades
Sealing Ring
Shaft
Turbine Disc
High Temperature Fasteners
Exotic Fasteners
Special Fasteners
| Alloy Name | Trade Name | UNS NO. | Germany Spec | French Spec | Specification |
| Waspaloy | / | N07001 | W.Nr.2.4654 | NC20K14 |
Waspaloy AMS5708 Waspaloy AMS5709 |
Waspaloy coefficient of thermal expansion
| θ/℃ | 20-100 | 20-200 | 20-300 | 20-400 | 20-500 | 20-600 | 20-700 | 20-800 | 20-900 |
| α | 12.47 | 12.73 | 13.04 | 13.53 | 13.97 | 14.47 | 15.05 | 15.68 | 15.95 |
Waspaloy thermal conductivity
| θ/℃ | 360 | 460 | 545 | 640 | 770 | 855 | 985 |
| W/(m·℃) | 16.8 | 18.3 | 20.2 | 22.4 | 24.1 | 25.3 | 28.0 |
Oxidation resistance in air with a duration of 100h
| θ/℃ | 900 | 1000 |
|
Oxidation rate g/(m2.h) |
0.083 | 0.226 |
Waspaloy welding
Can be fusion welded by argon-arc methods using a matched composition filler metal. If matching alloy is not available, then the nearest alloy richer in the essential chemistry (Ni, Co, Cr, Mo) shall be adopted.
Waspaloy machining
Heavy duty equipment and tooling shall be used to minimize work-hardening of it ahead of cutting.
Rincian kontak
Ohmalloy Material Co.,Ltd
Kontak Person: Mr. Qiu
Tel: +8613795230939
Mengirimkan permintaan Anda secara langsung kepada kami
Lebih Kawat Semprot Termal
-
Kawat aluminium penyemprotan termal
-
Kawat Semprot Termal Zn85Al15
-
Kawat Semprot Thermal Thermal Ni95Al5 1.6mm / 2mm Kinerja Tinggi Dengan ISO / CE
-
Restorasi Elemen Mesin Monel 400 Kawat Tahan Korosi Yang Baik
-
Nimonic80A. N07080 paduan 80A. W.S.2.4952
-
Inconel 625 Welding Wire ERNiCrMo-3 dengan Diameter 1,0 mm untuk aplikasi tahan korosi dan stabilitas suhu tinggi